- Cold-rolled steel
- Hot dip galvanized steel
- Aluminium-zinc coated steel
- Electrogalvanized steel
- Zinc-magnesium coated steel
Cold-rolled steel
Cold-rolled steel
Dimensions
Steel | Thickness, mm | Width, mm |
DC 01 | 0,5-3,0 | 1000-1500 |
DC 03 | 0,5-3,0 | 1000-1500 |
DC 04 | 0,5-3,0 | 1000-1500 |
DC 05 | 0,5-3,0 | 1000-1500 |
DC 06 | 0,5-3,0 | 1000-1500 |
DC 07 | 0,5-3,0 | 1000-1500 |
Tolerances
Tolerances according to EN 10131:2006. Ask for more information! |
Chemical composition and mechanical properties
Steel grade | Steel number | Chemical composition % | Mechanical properties | ||||||
C | P | S | Mn | Ti | Yield strength Rp 0,2 | Tensile strength, Rm (N/mm²) | Fracture elongation, A80 | ||
DC 01 | 1.0330 | 0,12 | 0,045 | 0,045 | 0,60 | – | 280 | 270 – 510 | 28% |
DC 03 | 1.0347 | 0,10 | 0,035 | 0,035 | 0,45 | – | 240 | 270 – 370 | 34% |
DC 04 | 1.0338 | 0,08 | 0,030 | 0,030 | 0,40 | – | 220 | 270 – 350 | 37% |
DC 05 | 1.0312 | 0,06 | 0,025 | 0,025 | 0,35 | – | 200 | 270 – 330 | 39% |
DC 06 | 1.0873 | 0,02 | 0,020 | 0,020 | 0,25 | 0,30 | 180 | 270 – 350 | 41% |
DC 07 | 1.0898 | 0,01 | 0,020 | 0,020 | 0,20 | 0,20 | 160 | 250 – 310 | 43% |
Surface finish and quality
Surface finish and quality | ||
A | normal surface | Imperfections such as small pits, different spangle sizes, dark spots, stripe-shaped marks, and small passivation defects are acceptable. Straightening and bending fractures and zinc runoff waves may be visible. |
B | improved surface | This type of surface is attained by skin passing. A small number of fractures in stretch forming direction, finishing imprints, scratches, impressions, spangle structures, zinc runoff waves and slight passivation errors may occur. |
Storage and warehousing
- Packaging must protect the material against defects and external influences.
- The material must have appropriate packaging for transportation.
- Max humidity 70%.
- Recommended storage temperature + 15…25Co.
- Min storage temperature + 5Co.
- Max temperature fluctuation 10 degrees
- Processing permitted if the material has reached a temperature of the plant.
- In winter, open the package when the material has reached a temperature of the plant, it is recommended to wait 4 days.
- NB! Warehousing indoors only.
Hot dip galvanized steel
Hot dip galvanized steel
Dimensions
Steel | Thickness, mm | Width, mm |
DX51D | 0,4-3,0 | 1000-1500 |
DX52D | 0,4-3,0 | 1000-1500 |
DX53D | 0,4-3,0 | 1000-1500 |
DX54D | 0,4-3,0 | 1000-1500 |
DX55D | 0,4-3,0 | 1000-1500 |
DX56D | 0,4-3,0 | 1000-1500 |
DX57D | 0,4-3,0 | 1000-1500 |
Coating
Coating | Weight g/m2 | |
+Z | zinc | 100-600 |
Tolerances
Tolerances according to EN 10143. Ask for more information! |
Chemical composition and mechanical properties
Steel grade | Chemical composition % | Mechanical properties | |||||||
C max | Si max | Mn | P | S | Ti | Yield strength Rp 0,2 | Tensile strength, Rm (N/mm²) | Fracture elongation, A80 | |
DX51D | 0,18 | 0,50 | 1,20 | 0,12 | 0,045 | 0,30 | – | 270 – 500 | 22% |
DX52D | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 140 – 300 | 270 – 420 | 26% |
DX53D | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 140 – 260 | 270 – 380 | 30% |
DX54D | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 220 | 260 – 350 | 36% |
DX55D | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 220 | 270 – 370 | 30% |
DX56D | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 180 | 260 – 350 | 39% |
DX57D | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 170 | 260 – 350 | 41% |
Surface finish and quality
Surface finish and quality | ||
M | reduced spangle | The finish is obtained by influencing the solidification process in a specific way. The surface will have reduced spangles, in some cases, not visible for the unaided eye. The finish will be ordered if the normal spangle does not satisfy the surface appearance requirements. |
A | normal surface | Imperfections such as small pits, different spangle sizes, dark spots, stripe-shaped marks, and small passivation defects are acceptable. Straightening and bending fractures and zinc runoff waves may be visible. |
B | improved surface | This type of surface is attained by skin passing. A small number of fractures in stretch forming direction, finishing imprints, scratches, impressions, spangle structures, zinc runoff waves and slight passivation errors may occur. |
Surface protection
Surface protection |
C | Chemically passivated | Chemical passivation protects the surface against humidity and reduces the risk of formation of corrosion products during storage or transportation. Local colour variations are permissible and do not impair the quality. |
Storage and warehousing
- Packaging must protect the material against defects and external influences.
- The material must have appropriate packaging for transportation.
- Max humidity 70%.
- Recommended storage temperature + 15…25Co.
- Min storage temperature + 5Co.
- Max temperature fluctuation 10 degrees
- Processing permitted if the material has reached a temperature of the plant.
- In winter, open the package when the material has reached a temperature of the plant, it is recommended to wait 4 days.
- NB! Warehousing indoors only.
Aluminium-zinc coated steel
Aluminium-zinc coated steel
Dimensions
Steel grade | Thickness, mm | Width, mm |
DX51D | 0,5-2,0 | 1000-1500 |
DX52D | 0,5-2,0 | 1000-1500 |
DX53D | 0,5-2,0 | 1000-1500 |
DX54D | 0,5-2,0 | 1000-1500 |
DX55D | 0,5-2,0 | 1000-1500 |
DX56D | 0,5-2,0 | 1000-1500 |
DX57D | 0,5-2,0 | 1000-1500 |
Coating
Coating | Weight g/m2 | |
+AZ | aluminum-zinc alloy | 150-185 |
Tolerances
Tolerances according to EN 10143:2006. Ask for more information! |
Chemical composition and mechanical properties
Steel grade | Steel number | Chemical composition | Mechanical properties | |||||||
C max | Si max | Mn | P | S | Ti | Yield strength Rp 0,2 | Tensile strength, Rm (N/mm²) | Fracture elongation, A80 | ||
DX51D | 1.0226 | 0,18 | 0,50 | 1,20 | 0,12 | 0,045 | 0,30 | – | 270 – 500 | 22% |
DX52D | 1.0350 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 140 – 300 | 270 – 420 | 26% |
DX53D | 1.0355 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 140 – 260 | 270 – 380 | 30% |
DX54D | 1.0306 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 220 | 260 – 350 | 36% |
DX55D | 1.0309 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 220 | 270 – 370 | 30% |
DX56D | 1.0322 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 180 | 260 – 350 | 39% |
DX57D | 1.0853 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 170 | 260 – 350 | 41% |
Surface finish and quality
Surface finish and quality | ||
M | reduced spangle | The finish is obtained by influencing the solidification process in a specific way. The surface will have reduced spangles, in some cases, not visible for the unaided eye. The finish will be ordered if the normal spangle does not satisfy the surface appearance requirements. |
A | normal surface | Imperfections such as small pits, different spangle sizes, dark spots, stripe-shaped marks, and small passivation defects are acceptable. Straightening and bending fractures and zinc runoff waves may be visible. |
B | improved surface | This type of surface is attained by skin passing. A small number of fractures in stretch forming direction, finishing imprints, scratches, impressions, spangle structures, zinc runoff waves and slight passivation errors may occur. |
Surface protection
Surface protection |
C | Chemically passivated | Chemical passivation protects the surface against humidity and reduces the risk of formation of corrosion products during storage or transportation. Local colour variations are permissible and do not impair the quality. |
Storage and warehousing
- Packaging must protect the material against defects and external influences.
- The material must have appropriate packaging for transportation.
- Max humidity 70%.
- Recommended storage temperature + 15…25Co.
- Min storage temperature + 5Co.
- Max temperature fluctuation 10 degrees
- Processing permitted if the material has reached a temperature of the plant.
- In winter, open the package when the material has reached a temperature of the plant, it is recommended to wait 4 days.
- NB! Warehousing indoors only.
Electrogalvanized steel
Electrogalvanized steel
Dimensions
Steel grade | Thickness, mm | Width, mm |
DC01 | 0,5-3,0 | 1000-1500 |
DC03 | 0,5-3,0 | 1000-1500 |
DC04 | 0,5-3,0 | 1000-1500 |
DC05 | 0,5-3,0 | 1000-1500 |
DC06 | 0,5-3,0 | 1000-1500 |
DC07 | 0,5-3,0 | 1000-1500 |
Coating
Coating | Thickness µm | Weight g/m2 |
+ZE 25/25 | 2,0 | 18 |
+ZE 50/50 | 5,0 | 36 |
+ZE 75/75 | 7,5 | 54 |
+ZE 100/100 | 1,0 | 72 |
Tolerances
Tolerances according to EN 10131:2006. Ask for more information! |
Chemical composition and mechanical properties
Steel grade | Steel number | Chemical composition % | Mechanical properties | ||||||||
C | P | S | Mn | Ti | Yield strength, Rp 0,2 | Tensile strength, Rm (N/mm²) | Fracture elongation, A80 | R90 min | N90 min | ||
DC01 | 1.0330 | 0,12 | 0,60 | 0,045 | 0,045 | – | 280 | 270-410 | 28% | – | – |
DC03 | 1.0347 | 0,10 | 0,45 | 0,035 | 0,035 | – | 240 | 270-370 | 34% | 1,3 | – |
DC04 | 1.0338 | 0,08 | 0,40 | 0,030 | 0,030 | – | 220 | 270-350 | 37% | 1,6 | 0,0170 |
DC05 | 1.0312 | 0,06 | 0,35 | 0,025 | 0,025 | – | 200 | 270-330 | 39% | 1,9 | 0,0190 |
DC06 | 1.0873 | 0,02 | 0,25 | 0,020 | 0,020 | 0,30 | 180 | 270-350 | 41% | 2,1 | 0,0210 |
DC07 | 1.0898 | 0,01 | 0,20 | 0,020 | 0,200 | 0,20 | 160 | 250-310 | 43% | 2,5 | 0,0220 |
Surface finish and quality
Surface finish and quality | ||
A | normal surface | Imperfections such as small pits, different spangle sizes, dark spots, stripe-shaped marks, and small passivation defects are acceptable. Straightening and bending fractures and zinc runoff waves may be visible. |
B | improved surface | This type of surface is attained by skin passing. A small number of fractures in stretch forming direction, finishing imprints, scratches, impressions, spangle structures, zinc runoff waves and slight passivation errors may occur. |
Storage and warehousing
- Packaging must protect the material against defects and external influences.
- The material must have appropriate packaging for transportation.
- Max humidity 70%.
- Recommended storage temperature + 15…25Co.
- Min storage temperature + 5Co.
- Max temperature fluctuation 10 degrees
- Processing permitted if the material has reached a temperature of the plant.
- In winter, open the package when the material has reached a temperature of the plant, it is recommended to wait 4 days.
- NB! Warehousing indoors only.
Zinc-magnesium coated steel
Zinc-magnesium coated steel
Dimensions
Steel grade | Thickness, mm | Width, mm |
DX51D+ZM | 1,2-3,0 | 1000-1500 |
DX52D+ZM | 1,2-3,0 | 1000-1500 |
DX53D+ZM | 1,2-3,0 | 1000-1500 |
DX54D+ZM | 1,2-3,0 | 1000-1500 |
DX55D+ZM | 1,2-3,0 | 1000-1500 |
DX56D+ZM | 1,2-3,0 | 1000-1500 |
DX57D+ZM | 1,2-3,0 | 1000-1500 |
Coating
Coating | Weight g/m² | Thickness µm/side |
ZM90 | 90 | 7 |
ZM120 | 120 | 9 |
ZM175 | 175 | 13 |
ZM195 | 195 | 16 |
ZM250 | 250 | 19 |
ZM310 | 310 | 24 |
Tolerances
Tolerances according to EN 10151. Ask for more information! |
Chemical composition and mechanical properties
Steel grade | Steel number | Chemical composition % | Mechanical properties | |||||||
C max | Si max | Mn | P | S | Ti | Yield strength Rp0,2 | Tensile strength, Rm (N/mm²) | Fracture elongation, A80 | ||
DX51D+ZM | 1.0226 | 0,18 | 0,50 | 1,20 | 0,12 | 0,045 | 0,30 | – | 270 – 500 | 22% |
DX52D+ZM | 1.0350 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 140 – 300 | 270 – 420 | 26% |
DX53D+ZM | 1.0355 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 140 – 260 | 270 – 380 | 30% |
DX54D+ZM | 1.0306 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 220 | 260 – 350 | 36% |
DX55D+ZM | 1.0309 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 220 | 270 – 370 | 30% |
DX56D+ZM | 1.0322 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 180 | 260 – 350 | 39% |
DX57D+ZM | 1.0853 | 0,12 | 0,50 | 0,60 | 0,10 | 0,045 | 0,30 | 120 – 170 | 260 – 350 | 41% |
Surface finish and quality
Surface finish and quality | ||
A | normal surface | Imperfections such as small pits, different spangle sizes, dark spots, stripe-shaped marks, and small passivation defects are acceptable. Straightening and bending fractures and zinc runoff waves may be visible. |
B | improved surface | This type of surface is attained by skin passing. A small number of fractures in stretch forming direction, finishing imprints, scratches, impressions, spangle structures, zinc runoff waves and slight passivation errors may occur. |
Storage and warehousing
- Packaging must protect the material against defects and external influences.
- The material must have appropriate packaging for transportation.
- Max humidity 70%.
- Recommended storage temperature + 15…25Co.
- Min storage temperature + 5Co.
- Max temperature fluctuation 10 degrees
- Processing permitted if the material has reached a temperature of the plant.
- In winter, open the package when the material has reached a temperature of the plant, it is recommended to wait 4 days.
- NB! Warehousing indoors only.